($Ti_{ 1-x}$$Al_{ x}$)N has been deposited on high speed steel (HSS) substrate using PECVD from the gas mixture of $TiC1_4$, $AlC1_4$, $NH_3$, $H_2$, and Ar. The correlation between the microstructure and the mechanical properties was investigated. ($Ti_{1-x}$$Al_{ x}$)N showed single phase NaCl-structure up to X=0.87, while a mixed phase of NaCl Type (Ti, Al) N and wurtzite structure AlN was observed for 0.87$Ti_{1-x}$ $Al_{x}$ )N became by degrees as increasing X, which made the hardness of the coating higher by Al addition. When the coating was composed of a mixed phase, however, the hardness decreased abruptly due to the effect of soft AlN phase. The wear volume of the coatings could be obtained as the concentration of the coating was varied, and the relation between the wear volume and hardness or the adhesion strength was discussed.