In this study, as an effort to improve the brittlement of coating layer, aluminum bronze coatings formed on steel substrates by arc jet spray process were subjected to post heat treatment. After each treatment, mechanical properties such as hardness, and UTS, and microstructural characterization of the specimens were investigated. The results showed that the hardness in the coatings slightly decreased with increasing heat treatment tine and temperature. The UTS of as-sprayed coatings was 4.31kgf/$ extrm{mm}^2$ and slightly increased to 5.51kgf/$ extrm{mm}^2$ after heat treatment at $900^{circ}C$ for 120min. On the other hand, the interdiffusion of copper and aluminum particles after heat treatment lead to decrease of the porosity density and increase the bond strength.

Arc jet coating, Aluminium bronze;Porosity;Thermal spray;Heat treatment;Surface hardening;