The microstructures and corrosion properties of Al-Si diffusion coated PWA1426 and PWA658 alloys have been investigated. The coated layer and corrosion properties were analysed by SEM, EDS and hot corrosion test. According to the results of SEM, it is supposed that the coated layers were composed of mixed, denuded and inter-diffusion layer. The coated PWA1426 alloy improved corrosion properties, compared to the PWA658 alloy. Corrosion debris generated during hot corrosion test of PWA658 alloy are identified as NiO, $TiO_2$and $NiAl_2$$O_4$from coated layer which increase oxidation rate and decrease adhesion. The PWA1426 alloy heat treated at $1080^{circ}C$ showed that NiAl and $Al_2$$O_3$formed on coated layer.