Reflective silver films with high quality were prepared on polyester substrate by using sputter deposit on techniques. Best reflectivity thin films of silver were produced with process parameters of $10^{-6}$ Torr as base pressure, 50 W as R.F. power, 5 mTorr as working pressure, and 10 sccm as Ar flow rate. Being deposited with an R.F. power of 50 W, Ag films revealed the highest 96.3 % reflectance as illuminated with a light of 700 nm wavelength. The adhesion of sample films showed as high as 14 to $20{;}kg/ extrm{cm}^2$, which is suitable for industrial purposes. Their film crystallinity and orientation resulted in the planes of (111) and (200) for the growth with a preferred orientation of <111>, in general. The cross-sections of thin film specimens showed columnar structures. It is noted that columns became coarsened and less dense as R.F. power increased, resulting in a low reflectivity for the product film.

silver film;thin reflective film;polyester substrate;sputter deposition;