저널

The iron-zinc interfacial reaction and corrosin properties in galvanizing bath containning Ni have been intestigated. The substrate steel plates were galvanized in Zn or Zn-0.018Al baths with various Ni contents. The corrosion resistance of galvanized specimens was also evaluated by $60^{circ}$bending test for galvannealing speaaimens. The corrosion resistance was improved with Ni addition in pure Zn bath, while deteriorated with Ni addition in Zn-0.18Al bath. The anti-powdering property, on thhe otherhand, was improved with Ni addition in Zn-0.18Al bath, while deteriorated with Ni addition in pure Zn. It was found that the anti-powdering property was improved with increasing $xi$ phase ratio in reaction layer.