A study on the Color and Texture of Ti$_{x}$N Coating with Sputtering Condition

Suputtering 조건에 따른 Ti$_{x}$N Coating 층의 색상과 집합조직에 관한 연구

김학동;조성식;

동양물산(주) 중앙기술 연구소;충남대학교 공과대학 금속공학과;

Abstract

Stainless is widely used for various purposes due to its good corrosion resistance. There has been much research to produce the color stainless steel by several methods. In this experiment, TixN films have been deposited on the SUS304 substrate by the DC magnetron sputtering system and the color and texture of the films as a function of coating conditions has been studies. The TixN films showed a (111) preferred orintation in bias-free conditions. The texture of coated later was changed from (111) to (200) to (2200 with a change of the bias from -1000V to -3000V. When the bias is low, coated elements have low energy. Therefore, the texturct (111) of low surface energy. The mobility of atoms was increased with the increase of the blas and texture was changed to the other plane. Non-etched specimens all exhibited strong (111) texture. This result shows that (111) is a loose plane and of non-etched specimens all exhibited. High growing velocity of (111) of especially was main texture of Non-etched specimens. Low working pressure($4 imes10^{-3}$torr) was more effective than figh working pressure ($6 imes10^{-3}$torr) for the gold color of $Ti_xN$ film. L and b were increased and a was decreased with the increase of bias voltage. Accordingly, We obtained the near gold color of $Ti_xN$ film(L;92, a;1~1.5 b:24~29.50. As a result of reflectance. And as the bias increased, the reflectance was proportional to the increasing bias voltage, but we took the top reflectance when the bias voltage was -200V.

Keywords