한국표면공학회지 (31권2호 73-80)

Pitting Corrosion Behavuor of N2+ ion Implanted AISI 316L Stainless Steel Compacts

질소 이온주입된 AiSi 316L 스테인리스강 소결체의 공식거동

최한철;

광양대학 제철금속과;

Abstract

The aim of this study is to develop sintered stainless steels (SSS) with good mechanical strength, wear resistance, and corrosion resistance by nitrogen ion implantation on the Culated SSS surface. Stainless steel compacts containg Cu (2-10 wt%) were prepared by electroless Cu-pating method which results in the increased3 homogenization in alloying powder. Nitrogen ion implantation was carried out by using N2 gas as the ion source. Nitrogen ions were embedded by an acceleratol of 130keV with doese $3.0 imes10^{17};ions/ extrm{cm}^2$ on the SSS at $25^{circ}C$ in$2 imes10^{-6}$ torr vacuum. The nitrogen ion implanted SSS obtained from anodic ploarization curves revealed higher corrosion potential than that of nitrogen ion unimplante one. And nitrogen ion implanted 316LSSS had good resistance to pitting corrosion due to the synergistic effect of Mo and N, and the inhibition of $NH_4;^+$, against $CI^-$.

Keywords