The development of colored surface on zinc coating by the oxidation of a melten alloy of zinc with a minor amount of oxygen-avid additive such as tianium has been studied. Using a galvanizing Zinc alloy containing 0.1 to 0.3wt%Ti, gold, purple or blue color was developed clearly and stably, depending upon the extent of oxidation, by air cooling after hot dipping in a bath at temperature of $550^{circ}C$ to $600^{circ}C$. The source of the color is light interference with surface oxide layer. THe final color depends on the thickness of the color depends on the thickness of $TiO_2$, played So compositing, temperature and time at elevated temperature after are all controlling variables. Since oxidation film such as $TiO_2$ played role of passivation film, the corrosion resistance in a colored galvanized steel sheet. It is also thought that surface oxide layer of $TiO_2$ inhibited dissolution of the coating layer.