Amorphous carbon nitride (a-C:N) multilayerfilms are formed by using altermating conditions during film deposition in are ion plating process. Because hard a-C:N films prepared with suitable megative bias voltages have large compressive stress, it is difficult to increase film thickness more than 200nm. Preparing multilayer films composed of hard layers and soft layers, we can grow thick multilayer films on Si and SKH steel substrate. The total thickness of multilayer films is more than 1$mu extrm{m}$. The multilayer films are several times thicker than the single layer films and almost equal in hardness and internal stress to the single layer ones. X-ray photoelectron spectroscopy(XPS) and Raman spectroscopy reveal that multilayer films equal to single layer films in structure, which is similar to the structure of DLC films.