한국표면공학회지 (29권3호 195-202)

Composition and Coercivity of Fe-Co-Ni Alloy Electrodeposits

Fe-Co-Ni합금박막의 조성 및 자기적 성질

예길촌;김용웅;문근호;

영남대학교 금속공학과;

Abstract

The composition, the microstructure and the magnetic properties(HC and Hk) of Fe-Co-Ni alloy electrodeposits were investigated according to the electrolysis conditions using sulfate bath paddle agitated. The current efficiency of the alloys electrodeposition was considerably low in the range of 16∼50%. The Fe content(wt.%) of the alloy increased from 20% to 57% with current density, while Ni content of them decreased in the range of 70∼24% respectively, and Co content was nearly constant. As a result, Fe/Ni ratio of the alloy increased from 0.3 to 2.0 showing the anomalous codeposition. The structure of the alloy changed from fcc to the mixed one of fcc+bcc with the increase of Fe/Ni ratio. The preferred orientation of the alloy with fcc and bcc structure were (220) and (110) respectively. The alloy with Fe/Ni ratio(0.3∼l.2) had the lowest coercivity of 0.4∼0.8 Oe.

Keywords