저널

A photoetching process is widely used for small and high precision parts in machinery, electronic and semi-conductor industries. One of the high precision parts, grid is very important part of digitron which use electron display, and it is fabricated by only photoetching process because of high precision. In this study, to develop high precision digitron grid, characteristics of etching solution were investigated with electrochemical test, that was potentiodynamic test and immersion test in the ferric chloride solution and added some additives. Based on the electrochemical etching test, grid was fabricated by continuous photoetching process at various etching condition. From the result of measured line width and etching depth under-cut and etching factor were calculated. For the fabrication of 25$mu extrm{m}$ line width, optimal etching condition was etching temperature 40~$45^{circ}C$, spray pressure 1.5kg/$ extrm{cm}^2$ and etching time 3~4min.