저널

The Ni-SiC composite plating was performed in a Watt nickel solution and the wear resistance of the composite layer was studied on a pin-on-flat type wear tester. The volume losses and friction coefficients were measured. It was found that the quantity of SiC powder in the composite layers was affected by SiC concentration, pH, temperature, and agitation speed in the Watt nickel solution. The hardness and wear resistance of the coatings increased with SiC content. The quantity of SiC powder in the coating from a nickel sulfamate solution is larger than that of the Watt nickel solution, because the amount of nickel ions absorbed on the SiC powder in the nickel sulfamate solution is greater than that in the Watt`s solution.