저널

The effect of nitrogen finishing for the control of coating weight in a nitrogen sealing box on the coating surface property in hot dip galvanizing process has been studied. The coated surface is free of oxide marks and edge overcoated. The coating uniformity is excellent ; the standard deviation of the coating thickness along width of the specimen was $1~1.2mu extrm{m}$ in the box whereas $2.5~3mu extrm{m}$ in the air. Considering surface quality of the coating such as oxide mark, edge overcoated and zinc dust, the oxygen content between 40 and 200 ppm was suggested in the box in addition the oxygen content of at least 40 ppm or the minimum dew point of $-27^{circ}C$ is required to prevent a zinc vaporization.