저널

Effects of deposition parameter on the ionic conductivity and structural change of the Lithium borosili-cate solid electrolyte films, prepared by rf sputtering using 7$LI_2O-3B_2O_3-1SiO_2$ single phase target and also a mosaic target enriched with $LI_2O$, were analyzed by measuring AC impedance and IR absorption spectra for the films. Thed solid electrolyte film deposited from the single phase target exhibited very low ionic conductivi-ty of $10^{-10}{Omega}^{-1}cm{-1}$ at room temperature, a result of low $Li^+$ ion content(7.52 at%) in the film. The $Li^+$ con-ductivity for the films deposited from the mosaic target, however, significantly increased to $10^{-7}{Omega}^{-1}cm{-1}$ due to both an increased $Li^+$content (14.75 at %) and a structural change of the films. The increased ionic conduc-tivity of the film appears to be associated with an easiness of ionic mobility by structural change of glassy film from a some close packed network structure to a open one. These structural changes of film were found to be closely related to the increase in the peak intensity at~$960cm^{-1}$ of IR absorption spectra for the glassy films. With increasing either argon pressure from 3 to 21 mtorr or rf power from 2 to 3 W/$cm^2$, the $Li^+$ conduc-tivity for the films significantly increased to an order of $10^{-6}{Omega}^{-1}cm{-1}$ due to an increase in openness of film structure, as confirmed by both an increase in the IR absorption peak intensity at ~$960cm^{-1}$ and a resultant reduction of activation energy for mobility of $Li^+$ ion.