Diffusion coating(metalliding) of aluminium on steel from molten fluorides(29.2wt.% LiF-11.7wt.% NaF-59.1wt.% KF, FLINAK) was studied. The electrolytic cell consists of a steel cathode and a consumable aluminium anode. Effects of manganese on the aluminium deposition were also investigated. The quality of the deposit was analyzed by SEM, OM, EPMA, EDXA, and also examined by means of Micro-Vickers hardness and corrosion tests. Deposit layer was identified as an aluminium-rich iron alloy caused by diffusion process. The optimum condition for the metalliding was found to be the current density, 50 to $150mA/ extrm{cm}^2$, the bath tem-perature, $57.5^{circ}C$, and the amount of AlF3, 10wt.%. Addition of manganese fluoride (up to 5wt.%) as a co-de-posit element improved significantly the quality of the deposit layer.