저널

P+ and BF2+ were implanted to LPCVD amorphous silicon films deposited on thermally-oxidized silicon wafers and the low temperature annealing process followed with various conditions to activate implanted ions and to recrystallize the films. We tried to find the optimum processing condition by comparing the recrystallization behaviors and the electrical properties. TEM analysis showed that the final grain size of BF2+-implanted films was similar to that of unimplanted films, whereas the grains of P+-implanted films. For both P+ - and BF2+ -implanted films, sheet resistances were decreased with elevating annealing temperature and the minimum value was about 110~120$Omega$/$square$ at $600^{circ}C$.