저널

The erosion characteristice of plasma-sprayed tungsten carbide chromium carbide coatings were investigated. Erosion tests were perfomed at room temperature by using Al2O3 and SiC particles accleerated in air stream. Weight losses of the coatings were measured over a range of paricle velocities and impingement angle. It was found that, for both of this coatings, the maximum erosion occurrd at a normal angle of impact, and the erosion rate at this impact angle was a power function of pparticle velocity. The values of the velocty emponent were between 3.07 and 3.50 Erosion value of chromium carbide coating was higher than that of tungsten carbide coating.