저널

Al-Si piston alloys such as AlS10CuMg have been anodized to examine apossibility of forming a hard film aat relatively higher temperatures compard with those in conventional sulfuric acid processes. Three types of electrolytes have been employed in this study ; electrolyte A(15% H2SO4, $0^{circ}C$), electrolyte B(12% H2SO4, 1% oxalic, $10^{circ}C$), electrolyte C(tartaric acid 125g/L+oxalic 75g/L+aluminum sulfate 225g/L, $25^{circ}C$). Hard anodisine process in electrolyte B at a current density of 1.54A/dm2 produced a harder film of VHN 396 at a relatibely low film forming voltage compared with those obtained in other electrolyte at equivalent current density. A liner relationship between hardness and abrasion resistance exists for Al-Si piston alloys. The hardness of anodized film decreasees with increasing silicon content in Al-Si alloys and also with bath temperature. The film hardeness of Na-modified alloy os higher than that of P-modified alloy due to its finer microstructre. The film on the silicon phase in Al-Si alloys is observed to be formed by lateral growth of oxide film nucleated at surroundings.