Sulfamate-chloride baths were fabricated to study the properties of the electrodeposited Ni and NiCo thin films. The dependences of current efficiency, deposit composition of Ni and Co, residual stress, surface morphology and microstructure of electrodeposited Ni and NiCo thin films on CoCl₂ concentration in sulfamate-chloride baths were investigated. The current efficiency was measured to be more than about 90%, independent of the changes of CoCl₂ concentration in the baths. Residual stress of Ni and NiCo thin films was increased from about 45 to about 250 MPa with varying CoCl₂ concentration from 0 to 0.210 M CoCl₂ in the baths and then reached to a plateau, about 250 MPa above 0.420 M CoCl₂ concentration. Nodular surface morphologies were observed at most CoCl₂ concentrations in the baths except 0.210 M. NiCo thin film electrodeposited from the bath with 0.210 M CoCl₂ concentration showed an acicular surface morphology. Pure Ni thin film consists of FCC(111), FCC(200), FCC(220), and FCC(311) peaks without any preferred orientation. On the other hand NiCo thin films make up of HCP(100), FCC(111), HCP(101), FCC(200), FCC(220) or HCP(110), FCC(311) or HCP(112) and FCC(222) peaks. It was revealed from the analysis of XRD result that FCC(111) peak at the NiCo thin film electrodeposited from the bath with 0.084 M CoCl₂ concentration can be regarded as the preferred orientation. However the peak of the preferred orientation was changed to FCC(220) or HCP(110) above 0.084 M CoCl₂ concentration in the baths. Then the intensity of FCC(220) or HCP(110) peak was gradually decreased with increasing CoCl₂ concentration further. The crystalline size of pure Ni thin film was observed to be about 53 ㎛ and those of NiCo thin films were in the range of 35~45 ㎛.

Electrodeposition;Ni thin film;NiCo thin film;sulfamate-chloride bath;thin film properties;