저널

The effect of boronizing on mechanical properties including wear behavior and hardness of Inconel 625 superalloy were investigated. The cross-section observation demonstrated that boronized samples were composed of multi-phase boride layer (Cr_xB_x, Ni₂B), diffusion layer, and substrate. The boride and diffusion layers were increased with increasing treatment temperature and holding time. However, Cr_xB_x layer was partially peeled off when it treated 1000℃. Subsequently, boride layer was completely separated from substrate with increasing temperature and time. A partial peeling of Cr_xB_x layer is not noticeably degraded mechanical properties. In particular, friction coefficient and wear resistance were enhanced in lack of Cr_xB_x phase. Therefore, these results suggest that a Ni₂B phase mainly contribute to wear behavior on boronized Inconel 625 superalloy.

Ni-based superalloy;Boronizing;Mechanical properties;Surface modification;