Investigation of Structural Change of DLC Coating during Frictional Wear by Raman Spectroscopy
라만 분광법을 활용한 마모 중 DLC 코팅의 구조적 변화 조사
김송희;장재철;
Kim, Song-Hee;Jang, Jae Cheol;
강원대학교 나노응용공학과;서울대학교 재료공학부;
Department of Nano Applied Engineering, Kangwon National University;School of Materials Science and Engineering, Seoul National University;
The structural change of DLC coatings during long-term wear test and dicing test under the low loading condition was investigated. DLC coatings were applied for the precision injection molds of a modified SNCM steel for the extension of life and the micro-diamond blades for the high cutting efficiency and the increase in life. A ball-on-disc wear tests in the mold steel and a dicing tests in the micro-diamond blades were conducted to understand degradation of DLC coatings. The degradation of DLC coatings for the injection mold steel and the micro-diamond blades during the wear and dicing tests were studied with Raman Spectroscopy. Raman peaks were divided two bands(D band and G band) to study the degradation process of DLC structure. By the wear test, polished condition of wear marks were observed to be maintained until 10 hrs of wear test period is given, but small striation marks appeared in 20 hours wear test. It was observed that
Diamond-like Carbon(DLC);Wear;Raman Analysis;ID/IG;Structural Change;