In order to improve corrosion resistance for cast stainless steel in seawater, the characteristics of corrosion resistance after plasma ion nitriding was investigated. Plasma ion nitriding process was conducted in a mixture of nitrogen of 25% and hydrogen of 75% at substrate temperature ranging from 350 to $500^{circ}C$ for 10 hours using pulsed-DC glow discharge plasma with working pressure of 250 Pa in vacuum condition. Corrosion tests were carried out for as-received and plasma ion nitrided specimens. The corrosion characteristics were investigated by measurement of weight loss and observation of surface morphology. In anodic polarization experiment, relatively less damage depth and weight loss were presented at a nitrided temperature of $400^{circ}C$, attributing to the formation of S-phase.

Corrosion resistance;Cast stainless steel;Seawater;Plasma ion nitriding;