Al1050 and Al7075 alloy specimens were exposed to atmospheric conditions for maximum 12 months and analyzed by Transmission Electron Microscopy (TEM) to characterize the early-stage corrosion behavior and thin surface oxide layers. By comparing of oxide films between Al1050 and Al7075 alloys, it is concluded that Al7075 has a relatively thicker surface oxide film than Al1050 but Al1050 has relatively more significant oxygen penetration through grain boundaries. The oxygen penetration through grain boundaries appeared to be influenced by intermetallic particles at the grain boundary. In the case of aluminum alloys, localized corrosion like pitting or intergranular corrosion should be considered as well as uniform corrosion when estimating the atmospheric corrosion rate.

Aluminum alloys;Atmospheric corrosion;TEM;Pitting corrosion;Intergranular corrosion;