NiO nanoparticles were synthesized by hydrothermal method for the application to ethanol gas sensor. They were composited with $Co_3O_4$ nanoparticles to improve the sensitivity to ethanol gas. Scanning electron microscopy revealed that the synthesized NiO nanoparticles were plate-shaped with the approximate size and thickness of 60 - 120 nm and 20 nm, respectively. On the other hand, $Co_3O_4$ nanoparticles mixed with NiO was observed to be spherical with the size range of 30 - 50 nm. The sensitivities of NiO sensors composited with $Co_3O_4$ nanoparticles at an optimal ratio of 8 : 2 were enhanced to approximately 1.44 - 1.79 times as high as those of as-synthesized NiO sensors for the ethanol concentration of 10 - 200 ppm at $200^{circ}C$. The mechanism of the improved ethanol gas sensing of the NiO sensors composited with $Co_3O_4$ nanoparticles was discussed.

NiO;$Co_3O_4$ nanoparticles;Ethanol;Gas sensor;