$Cu_2ZnSnSe_4$ thin films for solar absorber application were prepared by pulsed laser deposition of a synthesized $Cu_2ZnSnSe_4$ compound target. The film`s composition revealed that the deposited films possess an identical composition with the target material. Further film compositional control toward a stoichiometric composition was performed by optimizing substrate temperature, deposition time and target rotational speed. At the optimum condition, X-ray diffraction patterns of films showed that the films demonstrated polycrystalline stannite single phase with a high degree of (112) preferred orientation. The absorption coefficient of $Cu_2ZnSnSe_4$ thin films were above 104 cm.1 with a band gap of 1.45 eV. At an optimum condition, films were identified as a p type semiconductor characteristic with a resistivity as low as $10^{-1}{Omega}cm$ and a carrier concentration in the order of $10^{17}cm^{-3}$.

$Cu_2ZnSnSe_4$;Pulsed laser deposition;Stannite;Single phase;Solar absorber;Optical properties;