Anodizing to form oxide layers on the pure titanium was performed in the electrolyte containing 1.5M $H_2SO_4$, 0.2M $H_3PO_4$, and 2.5wt.% $CuSO_4$ using the ac-biased arc anodizing technique. Titanium oxide layers anodized with different applied voltages, voltage-elevating rates, and anodizing times were investigated. In addition, thermal oxidation test under an atmospheric environment for the arc-anodized specimens was carried out. The thickness of oxide layers were not affected by the voltage-elevating rates, but increased slightly with the increase of anodizing times. The thickness of oxide layers were increased with the increase of voltages, and increased remarkably in the condition of 200V. The size and number of the pore observed in the center of the porous cell were decreased with increase of applied voltage. From the result of thermal oxidation test, it revealed that oxide layer formed by arc anodizing more effective to prevent oxidation of pure titanium.

Titanium;Arc anodizing;Alternating current;Thermal oxidation;