저널

The Rates of formation and heats of activation for the intermatallic Compound Layers between Cold rolled sheet and molten aluminium &ath (adding small amounts of silicon) has been determined by Continous aluminizing method in the temperature range of 680$^{circ}$ to 760$^{circ}C$ and with immerssion time. The structure of the intermetallic Compound Layers was the shape of "Tongues" in pure Al-Bath and Al-Bath Containing 1% Si, But in Al-5% Si Bath was "Band" the Composition of the intermetallic Compound Layers were checked by microhardness measurements and X-Ray probe micro analyzer. FeAl intermetallic Compound layer was found to be uniform in pure Al-Bath and Al-5% Si Bath, But Fe Al intermetallic Compound Layer was shown in Al-1% Si Bath. The growth Rates of the intermetallic Compound Layers was most rapidly increased at Temperatures from 720$^{circ}$ to 760$^{circ}C$, at the immorsion time above 60 Second in pure Al-Bath, But in Al-1% Si Bath was solwly increased for the same conditions, and then in Al-5% Si Bath was hardly effected by these experimental condition. Heasts of activation of 29, 46 Kcal per mole which calculuted from Layer growth experiments were found in pure Al-Bath, Al-1% Si Bath respectively.