FT-IR and thermography were used to investigate the infrared radiation characteristic of SiO$_2$ film and SiO$_2$/Fe$_2$O$_3$film coated on aluminum. Through FT-TR spectrum, SiO$_2$film showed high infrared absorption in accordance with the stretching vibration of Si-O-Si, and as$ Fe_2$$O_3$was mixed additional absorption band appeared resulting from the stretching vibration of Fe-O at $590cm^{-1}$ and the bond of Si-O-Fe at $900 cm^{-1}$ The two kinds of film measured by the integration method and the reflective method coincided with each other in the wavelength area of infrared absorption and radiation, and corresponded well with Kirchhoff`s law as the infrared emissivity is high in wavelength where infrared absorption rate is high. The emissivity of $SiO_2$ film was 0.65 and that of $SiO_2$/Fe$_2$$O_3$film was 0.77, so the addition of$ Fe_2$$O_3$ raised the infrared emissivity by approximately 13%.$ SiO_2$$Fe_2$$O_3$ film is efficient as an infrared radiator at below $100^{circ}C$. The temperature of heat radiation after 7 minutes was 117$^{circ}C$ in aluminum plate and $155^{circ}C$ in $SiO_2$$Fe_2$$O_3$ film, $38^{circ}C$ higher than the former.

SiO$_2$/Fe$_2$O$_3$film;Infrared absorption;Reflectivity;infrared emissivity;FT-IR;