The surface morphology, the glossiness and the hardness of Zn-Cr and Zn-Cr-X(X:Co, Mn) alloy electrodeposits were investigated by using chloride bath with EDTA additive and flow cell system. The surface morphology of Zn-Cr alloy and Zn-Cr-Mn alloy changed from fine needle shape crystalline structure to colony structure of fine granular crystallites with increasing current density in the range of 20-100 $A/dm^2$. The surface morphology of Zn-Cr-Co alloy deposited from low Co concentration bath(2.5-10 g/$ell$) was similar to that of Zn-Cr alloy, while that of Zn-Cr-Co alloy deposited from high cobalt concentration bath was fine granular crystalline structure in the same range of current density. The glossiness of Zn-Cr and Zn-Cr-Mn alloy increased noticeably with increasing current density, while that of Zn-Cr-Mn alloy decreased with increasing Mn concentration of bath in high current density region. The glossiness of Zn-Cr-Co alloy deposited from low Co concentration bath increased with current density while that of the alloy from high Co concentration bath decreased with increasing current density. The hardness of Zn-Cr and Zn-Cr-X alloy increased noticeably with current density.

Zn-Cr-Zn-Cr-X alloy;Electrodeposits;Surface morphology;Glossiness;Hardness;